Synthesis and characterization of carbon-supported Pt-Ru-WOx catalysts by spectroscopic and diffraction methods.
In: Journal of Applied Electrochemistry.
Bd. 31
(2001)
Heft 7
.
- S. 793-798.
ISSN 1572-8838
DOI: https://doi.org/10.1023/A:1017585901064
Abstract
Carbon-supported Pt-Ru-WOx/C catalysts for application in PEMFC anodes were synthesized by a modified Bönnemann method. Their electrocatalytic activity for the oxidation of H2/CO mixtures and CH3OH was measured by E/i-curves in PEM single cell arrangements under working conditions. Information about composition, microstructure and nanomorphology was obtained by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), X-ray fluorescence analysis (XFA) and transmission electron microscopy (TEM). X-ray diffraction data at room temperature show only one single Pt f.c.c. phase; no evidence of Ru, W and their oxides, respectively, is found. Hence, the presence of W and Ru as amorphous oxide species seems likely. Surface-sensitive XPS measurements detect Pt0, platinum oxide and hydroxide species, metallic Ru, ruthenium oxide, hydrous ruthenium oxide and WO3. For the crystalline platinum phase particle sizes of less than 2 nm were determined by TEM images and XRD patterns via solving the Scherrer equation. Temperature-dependent XRD measurements were performed to show the influence of ageing on the catalyst structure.
Weitere Angaben
| Publikationsform: | Artikel in einer Zeitschrift |
|---|---|
| Begutachteter Beitrag: | Ja |
| Institutionen der Universität: | Fakultäten > Fakultät für Ingenieurwissenschaften > Lehrstuhl Werkstoffverfahrenstechnik > Lehrstuhl Werkstoffverfahrenstechnik - Univ.-Prof. Dr. Christina Roth Fakultäten Fakultäten > Fakultät für Ingenieurwissenschaften Fakultäten > Fakultät für Ingenieurwissenschaften > Lehrstuhl Werkstoffverfahrenstechnik |
| Titel an der UBT entstanden: | Nein |
| Themengebiete aus DDC: | 500 Naturwissenschaften und Mathematik > 540 Chemie 600 Technik, Medizin, angewandte Wissenschaften > 620 Ingenieurwissenschaften |
| Eingestellt am: | 22 Apr 2021 07:27 |
| Letzte Änderung: | 29 Jun 2022 09:08 |
| URI: | https://eref.uni-bayreuth.de/id/eprint/64867 |