Synthesis, Superstructure, Vacancy-Ordering of Intercalated Transition Metal Dichalcogenides

Title data

Ali, Sk Imran:
Synthesis, Superstructure, Vacancy-Ordering of Intercalated Transition Metal Dichalcogenides.
Bayreuth , 2014 . - 2, VI, 110 p.
( Doctoral thesis, 2014 , Universität Bayreuth, Fakultät für Mathematik, Physik und Informatik)

Official URL:

Abstract in another language

In this thesis, the synthesis and crystal structures are discussed of intercalated transition metal dichalcogenides (TMDCs) 6R-CuxTa1+yS2 and 2H-CuxTa1+ySe2, as well as the compound Cu3TaSe4. Synthesis of these compounds has been performed by the method of chemical vapor transport, using iodine as a transporting agent. X-ray diffraction may reveal superlattice reflections, which then indicates the existence of a superstructure. An eightfold superstructure has been found for 6R-CuxTa1+yS2 (x = 0.237, y = 0; x = 0.23, y = 0.06) and a fourfold superstructure has been found for 2H-Cu0:52TaSe2. 2H-Cu0:16Ta1:08Se2 and Cu3TaSe4 do not form any superstructure.

Abstract in another language

In dieser Arbeit wurden die Synthesen und Kristallstrukturen von Übergangsmetalldichalkogenide
(engl.: Transition Metal Dichalcogenides, TMDCs) 6R-CuxTa1+yS2 and 2H-CuxTa1+ySe2, sowie von der Verbindung Cu3TaSe4 untersucht. Die Synthese dieser Verbindungen wurde mit Hilfe des chemischen Transports (engl.: chemical
vapor transport, CVT) durchgef¨uhrt, wobei Jod als Transportmittel diente. Bei der Röntgenbeugung können Überstrukturreflexe auftreten, was auf die Existenz
einer Überstruktur hinweist. Für 6R-CuxTa1+yS2 (x = 0.237, y = 0; x = 0.23, y = 0.06) wurde eine achtfache Überstruktur und für 2H-Cu0:52TaSe2 wurde eine vierfache Überstruktur gefunden. 2H-Cu0:16Ta1:08Se2 und Cu3TaSe4 bilden keine Überstrukturen.

Further data

Item Type:	Doctoral thesis
Keywords:	Synthesis; Chemical-vapor-transport method; X-ray study; Superstructure; Vacancy-ordering
Institutions of the University:	Faculties Faculties > Faculty of Mathematics, Physics und Computer Science Faculties > Faculty of Mathematics, Physics und Computer Science > Department of Physics Faculties > Faculty of Mathematics, Physics und Computer Science > Group Material Sciences Faculties > Faculty of Mathematics, Physics und Computer Science > Group Material Sciences > Chair Crystallography Faculties > Faculty of Mathematics, Physics und Computer Science > Group Material Sciences > Chair Crystallography > Chair Crystallography - Univ.-Prof. Dr. Sander van Smaalen Graduate Schools Graduate Schools > University of Bayreuth Graduate School
Result of work at the UBT:	Yes
DDC Subjects:	500 Science > 530 Physics 500 Science > 540 Chemistry
Date Deposited:	08 Nov 2014 22:00
Last Modified:	15 May 2015 08:39
URI:	https://eref.uni-bayreuth.de/id/eprint/3433