Chakrapani, Kalapu ; Bendt, Georg ; Hajiyani, Hamidreza ; Lunkenbein, Thomas ; Greiner, Mark T. ; Masliuk, Liudmyla ; Salamon, Soma ; Landers, Joachim ; Schlögl, Robert ; Wende, Heiko ; Pentcheva, Rossitza ; Schulz, Stephan ; Behrens, Malte:
The Role of Composition of Uniform and Highly Dispersed Cobalt Vanadium Iron Spinel Nanocrystals for Oxygen Electrocatalysis.
In: ACS Catalysis.
Vol. 8
(2018)
Issue 2
.
- pp. 1259-1267.
ISSN 2155-5435
DOI: https://doi.org/10.1021/acscatal.7b03529
Abstract in another language
Cation substitution in transition-metal oxides is an important approach to improve electrocatalysts by the optimization of their composition. Herein, we report on phase-pure spinel-type CoV2-xFexO4 nanoparticles with 0 <= x <= 2 as a new class of bifunctional catalysts for the oxygen evolution (OER) and oxygen reduction reactions (ORR). The mixed-metal oxide catalysts exhibit high catalytic activity for both OER and ORR that strongly depends on the V and Fe content. CoV2O4 is known to exhibit a high conductivity, while in CoFe2O4 the cobalt cation distribution is expected to change due to the inversion of the spinel structure. The optimized catalyst, CoV1.5Fe0.5O4, shows an overpotential for the OER of similar to 300 mV for 10 mA cm(-2) with a Tafel slope of 38 mV dec(-1) in alkaline electrolyte. DFT+U+SOC calculations on cation ordering confirm the tendency toward the inverse spinel structure with increasing Fe concentration in CoV2-xFexO4 that starts to dominate already at low Fe contents. The theoretical results also show that the variations of oxidation states are related to the surface region, where the redox activity was found experimentally to be manifested in the transformation of V3+ -> V2+. The high catalytic activity, facile synthesis, and low cost of the CoV2-xFexO4 nanoparticles render them very promising for application in bifunctional electrocatalysis.
Further data
| Item Type: | Article in a journal |
|---|---|
| Refereed: | Yes |
| Additional notes: | WOS:000424735000066 |
| Institutions of the University: | Faculties > Faculty of Biology, Chemistry and Earth Sciences > Department of Chemistry Faculties Faculties > Faculty of Biology, Chemistry and Earth Sciences Faculties > Faculty of Biology, Chemistry and Earth Sciences > Department of Chemistry > Chair Operando-Analytics of Electrochemical Energy Storage > Chair Operando-Analytics of Electrochemical Energy Storage - Univ.-Prof. Dr. Thomas Lunkenbein Faculties > Faculty of Biology, Chemistry and Earth Sciences > Department of Chemistry > Chair Operando-Analytics of Electrochemical Energy Storage |
| Result of work at the UBT: | No |
| DDC Subjects: | 500 Science > 540 Chemistry |
| Date Deposited: | 13 Jun 2025 07:40 |
| Last Modified: | 04 Jul 2025 11:32 |
| URI: | https://eref.uni-bayreuth.de/id/eprint/93716 |