Zeng, Jun ; Hou, Haoqing ; Wendorff, Joachim H. ; Greiner, Andreas:
Poly(vinyl alcohol) nanofibres by electrospinning: influence of molecular weight on fibre shape.
In: e-Polymers.
Bd. 5
(2005)
Heft 1
.
- 38.
ISSN 1618-7229
DOI: https://doi.org/10.1515/epoly.2005.5.1.387
Volltext
Abstract
Poly(vinyl alcohol) (PVA) nanofibres were obtained by electrospinning of PVA/water solutions. Formation of beaded fibres combined with decreased fibre diameters was observed for low PVA concentrations. Electrospinning of blends of PVA of different molecular weight resulted in less bead formation and smaller fibre diameters as compared to corresponding homopolymers of similar viscosity.
Weitere Angaben
| Publikationsform: | Artikel in einer Zeitschrift |
|---|---|
| Begutachteter Beitrag: | Ja |
| Keywords: | POLYMER TEMPLATE FIBERS; JETS |
| Institutionen der Universität: | Fakultäten > Fakultät für Biologie, Chemie und Geowissenschaften > Fachgruppe Chemie > Lehrstuhl Makromolekulare Chemie II > Lehrstuhl Makromolekulare Chemie II - Univ.-Prof. Dr. Andreas Greiner Fakultäten Fakultäten > Fakultät für Biologie, Chemie und Geowissenschaften Fakultäten > Fakultät für Biologie, Chemie und Geowissenschaften > Fachgruppe Chemie Fakultäten > Fakultät für Biologie, Chemie und Geowissenschaften > Fachgruppe Chemie > Lehrstuhl Makromolekulare Chemie II |
| Titel an der UBT entstanden: | Nein |
| Themengebiete aus DDC: | 500 Naturwissenschaften und Mathematik > 540 Chemie |
| Eingestellt am: | 13 Apr 2015 08:28 |
| Letzte Änderung: | 21 Dec 2023 10:28 |
| URI: | https://eref.uni-bayreuth.de/id/eprint/9699 |