Schönauer-Kamin, Daniela ; Hetzel, Kevin ; Bresch, Sophie ; Moos, Ralf:
Powder-Aerosol deposited (PAD) calcium manganate as n-type thermoelectric material.
2022
Veranstaltung: 18th European Conference on Thermoelectrics, ECT'22
, 14.-16. Sept. 2022
, Barcelona, Spain.
(Veranstaltungsbeitrag: Kongress/Konferenz/Symposium/Tagung
,
Poster
)
Abstract
Currently, calcium manganate CaMnO3 and calcium cobaltite Ca3Co4O9 are being investigated as n-type resp. p-type semiconducting materials as oxidation- and temperature-resistant thermoelectric materials for oxide multilayer thermoelectric generators (TEGs). In order to manufacture multilayer TEGs, pressure-assisted sintering processes at high temperatures are necessary to achieve optimal thermoelectric material properties. To realize TEGs in planar film technology, another method to obtain dense ceramic layers directly from the synthesized starting powders without a subsequent high temperature step is emerging recently: the powder aerosol deposition (PAD) method. In the present work, it is investigated whether PAD is suitable to produce dense ceramic films from Smdoped CaMnO3 and Ca3Co4O9 powders. The resulting thermoelectric properties are characterized as a function of temperature. CaMnO3 powder could successfully be processed by PAD with resulting layer thicknesses of 5-6 μm without any high-temperature sintering steps of the films. The electrical conductivity and the Seebeck coefficient of the films were determined in-plane from room temperature to 600 °C in air. The results show a Seebeck coefficient of around -200 μV/K, which is comparable to results of pressed and sintered bars. At 400 °C, the electrical conductivity corresponds to the conductivity of the bar. At higher temperatures the conductivity is better than with the reference. Below 400°C, the electrical conductivity is somewhat lower than that of the reference sample, a mild thermal treatment of the PAD layer improves it. It is expected that the thermal conductivity of the PAD film will be lower compared to the bars due to the nano-crystalline film morphology. This should result in a significantly increased ZT value for the PAD layers and a higher efficiency of the TEG. The work shows that both CaMnO3 and Ca3Co4O9 can be successfully processed by PAD, and the PAD films show comparable thermoelectric properties.
Weitere Angaben
| Publikationsform: | Veranstaltungsbeitrag (Poster) |
|---|---|
| Begutachteter Beitrag: | Ja |
| Institutionen der Universität: | Fakultäten > Fakultät für Ingenieurwissenschaften Fakultäten > Fakultät für Ingenieurwissenschaften > Lehrstuhl Funktionsmaterialien > Lehrstuhl Funktionsmaterialien - Univ.-Prof. Dr.-Ing. Ralf Moos Profilfelder > Advanced Fields > Neue Materialien Forschungseinrichtungen > Forschungszentren > Bayreuther Materialzentrum - BayMAT Fakultäten Fakultäten > Fakultät für Ingenieurwissenschaften > Lehrstuhl Funktionsmaterialien Profilfelder Profilfelder > Advanced Fields Forschungseinrichtungen Forschungseinrichtungen > Forschungszentren |
| Titel an der UBT entstanden: | Ja |
| Themengebiete aus DDC: | 600 Technik, Medizin, angewandte Wissenschaften > 620 Ingenieurwissenschaften |
| Eingestellt am: | 27 Sep 2022 08:21 |
| Letzte Änderung: | 27 Sep 2022 08:21 |
| URI: | https://eref.uni-bayreuth.de/id/eprint/71981 |